WebMar 15, 1997 · At room temperature, a slightly rectified I-V characteristic curve is obtained, while at 200°C and above, the I-V curve is linear. For all the p-GaN samples, it is also found that the sheet resistance decreases by an order of magnitude with increasing temperature from 25°C to 350°C. Webmemory behaviors in the epitaxially regrown GaN-on-GaN vertical p-n diodes, which have not been reported before, to the best of our knowledge. The device showed repro-ducible switching behaviors with good endurance performance of 1000 cycles test at both room temperature and 300 °C. The set voltage increased with temperature and remained stable
Thermal stability of Pt, Pd, Ni on GaN — Arizona State University
WebApr 1, 1997 · We report on the thermal stability of Pt and Pd thin films on GaN up to 800 °C. We have found that for Pt thin films submicron size metal spheres form at temperatures … WebIn this study, we mechanistically investigated the dehydrogenation reaction of decalin to tetralin to naphthalene on Pd and Pt catalysts using density functional theory (DFT) calculations combined with experimental validation. We firstly explored the relative energy profile of the entire elementary steps of the dehydrogenation reaction. highland golf course tacoma wa
Temperature Behavior of Pt/Au Ohmic Contacts to p-GaN
WebMetals like Pt, Ni, Pd, and Au which have high work function than GaN make a better choice for gate con-tact. Pt has a high work function (5.65 eV) that makes it ideal for use as Schottky contacts on n-type GaN, and it is also resistant to oxidation and corrosion [1]. There are only a few reports on Pt/GaN Schottky barrier di-odes. WebJun 25, 2016 · reaching the Pt/GaN interface with increasing temperature. In conclusion, Pt-coated multiple GaN nanowires operated at low bias (0.1V) are not as effective as sensors for detection of ppm hydrogen at room temperature as similar Pd-coated nanowire sen-sors. Pt-coated nanowires showed a marked decrease in sensitivity WebNo reactions occur in the Pt, Pd, and Ni systems with annealing up to 800°C. The Pt film begins to form submicron spheres and islands after annealing above 600°C. The Pd and … highland golf course washington